Ranges from 15 MPa to 25 MPa, depending on mix ratio and curing quality. PCC is strong in compression and ideal for load-bearing applications.
Relatively low, approximately 10% of its compressive strength. Since PCC lacks reinforcement, it is weak in tension and prone to cracking under tensile stress.
Typically around 25 to 30 GPa, indicating the stiffness of concrete under load.
Varies between 2200 to 2400 Kg/m³, based on aggregate and mix design.
Drying shrinkage can occur over time, which may lead to surface cracks without proper curing or joint placement.
Offers good durability in compression when properly mixed and cured, making it suitable for foundations, floors, and pavements.